High Fire Retardant Rigid Foam Blend Polyols by 141b Base

• Customization: Available
• CAS No.: 9003-11-6
• Formula: C5h10o2
• Model NO.: Vpipe-2A
• EINECS: 618-355-0
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Blue
• Transport Package: 200kg/Drum
• Trademark: VICUSVIDA
• Origin: China
• HS Code: 3907299090
• Production Capacity: 10000 Tons/Year

Product Description

 

Product Introduction
Vpipe-2A is a kind of high fire retardant rigid foam blend polyols by 141b base, reacting with  MDI  to  be  rigid  foam,which  is  even  foam  cell,  low thermal insulation,high fire retardant,no shrinkage in low temperature,
widely used in stream heat pipe,LNG, and other low temperature insulation project and so on.

Physical Property

Appearance		Light yellow transparent viscous liquid
Hydroxyl value	mgKOH/g	150-250
Dynamic viscosity   (25ºC)	mPa.S	150-300
Density         (20ºC)	g/ml	1.20- 1.30
Storage temperature	ºC	10-25
Storage stability	Month	6

Recommended Ratio

Raw Material	Pbw
Vpipe-2A blend polyols Isocyanate	100 100

Technology and Reactivity

Items		Manual mixing
Material temperature	ºC	20
Moulding temperature	ºC	25
cream time	s	20-30
Gel time	s	145- 185
Demold time	min	15
Free Density	kg/m3	23-24

Foam Performances

Foam density by moulding Closed cell rate Thermal conductivity(15ºC) Compressive Strength (perpendicular to the direction of rising) Dimensional Stability (24h,-20 ºC) (24h, 100 ºC)

ASTM D1622 ASTM D1940 ASTM C518 ASTM D 1621 ASTM D2126 ASTM D2126

30-35kg/m3 ≥90% ≤22mW/(m.K) 150- 180kPa ≤1.0% ≤1.5%